TECHINCAL DATA
Explore the tabs below for each of the raw materials used in our exterior & interior mouldings.
TYPE I EPS (Exterior Mouldings)
PHYSICAL PROPERTIES
Density lb/ft3
ASTM D1622 - 1.0 lb/ft3
Density lb/ft3
ASTM D1622 - 16.0 Kg/m3
R-Value/1-inch @ 75°F
ASTM C518 - 3.9 ft2·h·°F/BTU
RSI/25mm @ 24°C
ASTM C518 - 0.65 (m2·°K/W)
R-Value/1-inch @ 0°F
ASTM STP1320 - 4.6 ft2·h·°F/BTU
RSI/25mm @ -18°C
ASTM STP1320 - 0.81 (m2·°K/W)
Compressive strength at 10% strain
ASTM D1621 - 12.5 psi (86.0 kPa)
Flexural strength
ASTM C203 - 27.8 psi (192.0 kPa)
Water absorption (% by volume)
ASTM D2842 - 3.8%
Water vapor permeance
ASTM E96 - 282.0 ng/Pa.s.m2 (4.95 perms)
Dimensional Stability Linear change
ASTM D2126 -1.5%
Limiting Oxygen Index
ASTM D2863 ->24%
TYPE II EPS (INTERIOR Mouldings)
PHYSICAL PROPERTIES
Density lb/ft3
ASTM D1622 - 1.4 lb/ft3
Density lb/ft3
ASTM D1622 - 22.0 Kg/m3
R-Value/1-inch @ 75°F
ASTM C518 - 4.0 ft2·h·°F/BTU
RSI/25mm @ 24°C
ASTM C518 - 0.70 (m2·°K/W)
R-Value/1-inch @ 0°F
ASTM STP1320 -4.8 ft2·h·°F/BTU
RSI/25mm @ -18°C
ASTM STP1320 - 0.84 (m2·°K/W)
Compressive strength at 10% strain
ASTM D1621 - 12.5 psi (86.0 kPa)
Flexural strength
ASTM C203 - 45.0 psi (310.0 kPa)
Water absorption (% by volume)
ASTM D2842 - 1.87%
Water vapor permeance
ASTM E96 - 187.23 ng/Pa.s.m2 (3.29 perms)
Dimensional Stability Linear change
ASTM D2126 -1.5%
Limiting Oxygen Index
ASTM D2863 ->24%
PHYSICAL PROPERTIES
Construction
ASTM D-3775
Warp: 5.0 (per inch) / 19.4 (per 10cm)
Weft: 4.5 (per inch) /17.3 (per 10cm)
Weight
ASTM D-3776
2.6 (oz/yd2) / 86.5 (g/m2)
Thickness
ASTM D-1777
0.015 (per inch) / 0.380 (per mm)
Minimum Tensile
ASTM D-5035
Warp: 130 (lb/in) / 580 (N/2.54cm)
Weft: 30 (lb/in) / 150 (N/2.54cm)
Weave
Hurl Leno
The Mouldex Mouldings basecoat is a two-component polymer-based cementitious base coat consisting of a water-based acrylic liquid component mixed with a dry component.
Trim Coat mix utilizes advanced polymer technology combining the strength and toughness of polymer-modified cement with the flexibility of synthetics.
The application is completed in a our factory controlled environment under optimal conditions.
We have formulated our basecoat to provide a highly flexible cementitious coating which is very crack resistant. It can be bent over a 6.4 mm (1/4”) mandrel without cracking.
FEATURES
• Superior adhesion to various inorganic substrates
• Combines the strength of cement with the flexibility of synthetics
• Designed to allow minor movements in the substrate without causing cracking in the base coat
• Excellent job site quality control
PHYSICAL PROPERTIES
Product Type: Water-based acrylic, sand-filled mixture
pH Level: 9.0 to 9.5
Toxicity: Non-toxic
PERFORMANCE PROPERTIES
Fire Ratings: (For non-combustible moulding performance)
Class A: Flame Spread = 25, Smoke Dev. = 110, Helps Meet ASTM E-84, UL 263
Class B: Flame Spread = 35, Smoke Dev. = 120, Helps Meet ASTM E-84, UL 263
*The above is available as an option at no extra cost and must be requested at time of order placement.
Tensile Strength
ASTM C109 - 0.35 MPa (50 psi) without mesh
ASTM C109 - 16.55 MPa (2400 psi) with mesh
Elongation
ASTM D412 - 9.4%
Flexural Strength
ASTM C293 - 8.28 MPa (1200 psi)
Air Leakage
ASTM E283 - 0.0022 L/s.m2@ 3.0 mm thick
Water Vapour Permeance
ASTM E96 - 370 ng/Pa.s.m2 @ 25°C
Impermeability to Water
CCMC 6.7 - Pass
Coefficient of Water Absorption
CCMC 5.5.1 - 0.00007 kg/(m2.s1/2)
Salt Spray Resistance
ASTM B117 - Passed (300 hours)
Accelerated Weathering
ASTM D822 - Passed (2000 hours)
Freeze/Thaw Resistance
CMC Method - Passed (10 cycles)